ASTM A234 Grade WP115 Heat-Treated
ASTM A234 Grade WP115 Heat-Treated general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.8 g/cm³ | Typical for Steel |
ASTM A234 Grade WP115 Heat-Treated thermal
| Property | Value |
|---|---|
| Carbon | Carbon of 0.08 - 0.13 % |
| Chromium | Chromium of 10 - 11 % |
| Copper | Copper of 0.1 % |
| Manganese | Manganese of 0.2 - 0.5 % |
| Molybdenum | Molybdenum of 0.4 - 0.6 % |
| Nickel | Nickel of 0.25 % |
| Phosphorus | Phosphorus of 0.02 % |
| Silicon | Silicon of 0.15 - 0.45 % |
| Sulfur | Sulfur of 5E-3 % |
ASTM A234 Grade WP115 Heat-Treated mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 190 - 210 GPa | Typical for Steel |
| Elongation A50 | 23.0 °C | Elongation A50 of 13 - 20 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Steel |
| Tensile strength | 23.0 °C | Tensile strength of 620 MPa | - |
| Yield strength Rp0.2 | 23.0 °C | Yield strength Rp0.2 of 450 MPa | - |