ASTM A232 Annealed and Cold-Drawn or Oil-Tempered
ASTM A232 Annealed and Cold-Drawn or Oil-Tempered general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.8 - 7.9 g/cm³ | Typical for Chromium Vanadium Steel |
ASTM A232 Annealed and Cold-Drawn or Oil-Tempered thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 23.0 °C | Coefficient of thermal expansion of 1.2E-5 1/K | Typical for Chromium Vanadium Steel |
| Melting point | - | Melting point of 1382 - 1529 °C | Typical for Chromium Vanadium Steel |
ASTM A232 Annealed and Cold-Drawn or Oil-Tempered electrical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.48 - 0.53 % |
| Chromium | Chromium of 0.8 - 1.1 % |
| Manganese | Manganese of 0.7 - 0.9 % |
| Phosphorus | Phosphorus of 0.02 % |
| Silicon | Silicon of 0.15 - 0.35 % |
| Sulfur | Sulfur of 0.035 % |
| Vanadium | Vanadium of 0.15 % |
ASTM A232 Annealed and Cold-Drawn or Oil-Tempered mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 200 - 215 GPa | Typical for Chromium Vanadium Steel |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.29 [-] | Typical for Chromium Vanadium Steel |
| Reduction of area | 23.0 °C | Reduction of area of 40 - 45 % | - |
| Tensile strength | 23.0 °C | Tensile strength of 1320 - 2260 MPa | - |