ASTM A227 Class I Cold Drawn

Equivalent material: ASTM I, UNS K06501, UNS K07001, UNS K24045

ASTM A227 Class I Cold Drawn general

Property Temperature Value Comment
Density 23.0 °C Density of 7.8 - 7.9 g/cm³ Typical for High Carbon Steel

ASTM A227 Class I Cold Drawn thermal

Property Temperature Value Comment
Coefficient of thermal expansion 23.0 °C Coefficient of thermal expansion of 1.32E-5 1/K Typical for High Carbon Steel
Max service temperature - Max service temperature of 500 °C Typical for Carbon Steel
Melting point - Melting point of 1289 - 1478 °C Typical for High Carbon Steel
Specific heat capacity 23.0 °C Specific heat capacity of 486 J/(kg·K) Typical for High Carbon Steel
Thermal conductivity 23.0 °C Thermal conductivity of 36 W/(m·K) Typical for High Carbon Steel

ASTM A227 Class I Cold Drawn magnetic

Property Value
Carbon Carbon of 0.45 - 0.85 %
Manganese Manganese of 0.3 - 1.3 %
Phosphorus Phosphorus of 0.04 %
Silicon Silicon of 0.15 - 0.35 %
Sulfur Sulfur of 0.05 %

ASTM A227 Class I Cold Drawn electrical

Property Temperature Value Comment
Electrical resistivity 23.0 °C Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m Typical for Carbon Steel

ASTM A227 Class I Cold Drawn mechanical

Property Temperature Value Comment
Elastic modulus 23.0 °C Elastic modulus of 200 - 215 GPa Typical for High Carbon Steel
Poisson's ratio 23.0 °C Poisson's ratio of 0.29 [-] Typical for High Carbon Steel
Shear modulus 23.0 °C Shear modulus of 81 GPa Typical for High Carbon Steel
Tensile strength 23.0 °C Tensile strength of 1010 - 2240 MPa -

Contact us

Henan Bebon Iron&Steel Co., Ltd.

Xicheng Science & Technology Building High-tech Development Zone, Zhengzhou, China

Tel: +86-371-86151827

E-Mail: [email protected]

PlaceholderContact us

Message