ASTM A213 Grade T5
Equivalent material: DIN 1.7362, DIN 12 CrMo 19 5, DIN X11CrMo5, DIN 12CrMo19-5, DIN X12CrMo5, AFNOR Z10CD5.05, BS 3606-625, BS X11CrMo5, BS X12CrMo5, UNI 16CrMo205, JIS SFVAF5A, JIS SFVAF5B, JIS STPA25, JIS STBA25, JIS STFA25, JIS SCMV6, JIS SFVAF5C, JIS SFVAF5D, JIS SNB5, EN X12CrMo5, EN X11CrMo5, EN 1.7362, ISO X12CrMo5, ISO X12CrMo5-1, ISO F37, ASTM Grade B5, ASTM Grade P5
ASTM A213 Grade T5 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Chromium Molybdenum Steel |
ASTM A213 Grade T5 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.1E-5 - 1.4E-5 1/K |
Typical for Chromium Molybdenum Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Molybdenum Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 448 - 502 J/(kg·K) |
Typical for Chromium Molybdenum Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 - 43 W/(m·K) |
Typical for Chromium Molybdenum Steel |
ASTM A213 Grade T5 electrical
| Property |
Value |
| Carbon |
Carbon of 0.15 % |
| Chromium |
Chromium of 4 - 6 % |
| Manganese |
Manganese of 0.3 - 0.6 % |
| Molybdenum |
Molybdenum of 0.45 - 0.65 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.5 % |
| Sulfur |
Sulfur of 0.025 % |
ASTM A213 Grade T5 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Chromium Molybdenum Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Molybdenum Steel |