ASTM A213 Grade T24 Heat-Treated
Equivalent material: ASTM F24, UNS K30736
ASTM A213 Grade T24 Heat-Treated general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.8 g/cm³ | Typical for Steel |
ASTM A213 Grade T24 Heat-Treated thermal
| Property | Value |
|---|---|
| Aluminium | Aluminium of 0.02 % |
| Boron | Boron of 1.5E-3 - 7E-3 % |
| Carbon | Carbon of 0.05 - 0.1 % |
| Chromium | Chromium of 2.2 - 2.6 % |
| Manganese | Manganese of 0.3 - 0.7 % |
| Molybdenum | Molybdenum of 0.9 - 1.1 % |
| Nitrogen | Nitrogen of 0.01 % |
| Phosphorus | Phosphorus of 0.02 % |
| Silicon | Silicon of 0.15 - 0.45 % |
| Sulfur | Sulfur of 0.01 % |
| Vanadium | Vanadium of 0.2 - 0.3 % |
ASTM A213 Grade T24 Heat-Treated mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 190 - 210 GPa | Typical for Steel |
| Elongation A50 | 23.0 °C | Elongation A50 of 20 % | - |
| Hardness, Brinell | 23.0 °C | Hardness, Brinell of 250 [-] | - |
| Hardness, Rockwell C | 23.0 °C | Hardness, Rockwell C of 25 [-] | - |
| Hardness, Vickers | 23.0 °C | Hardness, Vickers of 265 [-] | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Steel |
| Tensile strength | 23.0 °C | Tensile strength of 585 MPa | - |
| Yield strength | 23.0 °C | Yield strength of 415 MPa | - |