ASTM A213 Grade T23 Heat-Treated
Equivalent material: ASTM F23, UNS K40712
ASTM A213 Grade T23 Heat-Treated general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.8 g/cm³ | Typical for Steel |
ASTM A213 Grade T23 Heat-Treated thermal
| Property | Value |
|---|---|
| Aluminium | Aluminium of 0.03 % |
| Boron | Boron of 1E-3 - 6E-3 % |
| Carbon | Carbon of 0.04 - 0.1 % |
| Chromium | Chromium of 1.9 - 2.6 % |
| Manganese | Manganese of 0.1 - 0.6 % |
| Molybdenum | Molybdenum of 0.05 - 0.3 % |
| Nickel | Nickel of 0.4 % |
| Niobium | Niobium of 0.02 - 0.08 % |
| Nitrogen | Nitrogen of 0.02 % |
| Phosphorus | Phosphorus of 0.03 % |
| Silicon | Silicon of 0.5 % |
| Sulfur | Sulfur of 0.01 % |
| Tungsten | Tungsten of 1.45 - 1.75 % |
| Vanadium | Vanadium of 0.2 - 0.3 % |
ASTM A213 Grade T23 Heat-Treated mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 190 - 210 GPa | Typical for Steel |
| Elongation A50 | 23.0 °C | Elongation A50 of 20 % | - |
| Hardness, Brinell | 23.0 °C | Hardness, Brinell of 220 [-] | - |
| Hardness, Rockwell B | 23.0 °C | Hardness, Rockwell B of 97 [-] | - |
| Hardness, Vickers | 23.0 °C | Hardness, Vickers of 230 [-] | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Steel |
| Tensile strength | 23.0 °C | Tensile strength of 510 MPa | - |
| Yield strength | 23.0 °C | Yield strength of 400 MPa | - |