AISI 316 Cold Finished
Equivalent material: DIN 1.4401, DIN 316S42, DIN 316S33, DIN X5CrNiMo17-12-2, DIN X 5 CrNiMo 18 10, AFNOR Z7CND17-11-02, BS 316S16, UNI X5CrNiMo1712, SS 2347, UNE F.3543, SAE 316, JIS SUS316, JIS SUS316TKA, JIS SUS316TF, JIS SUS316FB, JIS SUSF316, JIS SUS316TKC, JIS SUS316TP, JIS SUS316TB, JIS SUS316TBS, JIS SUS316TPY, JIS SUS316TPD, JIS SUS316HTP, JIS SUS316HTB, JIS SUS316HTF, JIS SUS316F, EN X5CrNiMo17-12-2, EN 1.4401, ISO A4, GOST 0Cr17Ni12Mo2, GB 08Ch27N13M2, ASTM 316, UNS S31600, IS X04Cr17Ni12Mo2, DIN 1.4436, DIN X5CrNiMo17-13-3, DIN X3CrNiMo17-13-3, AFNOR Z7CND18-12-03, BS 316S13, UNI X8CrNiMo1713, SS 2343, JIS SCS14, EN X3CrNiMo17-13-3, EN 1.4436, ISO A5, DIN 1.4984, AFNOR 9165-041, AFNOR 9165 25, AFNOR Z 10 CNW 17, EN 1.4984, ASTM F316, ASTM S31600, ASTM TP316, ASTM B8M, ASTM Grade HE35, ASTM Grade 8M, ASTM FP316, ASTM MT316, ASTM Grade 8MA, ASTM Grade B8M, ASTM Grade B8MA, ASTM Grade B8M2, ASTM Grade B8M3
AISI 316 Cold Finished general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.9 g/cm³ |
AISI 316 Cold Finished thermal
| Property |
Temperature |
Value |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.6E-5 1/K |
| Melting point |
- |
Melting point of 1380 °C |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 490 J/(kg·K) |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 15 W/(m·K) |
AISI 316 Cold Finished magnetic
| Property |
Value |
| Carbon |
Carbon of 0 - 0.08 % |
| Chromium |
Chromium of 16 - 18.5 % |
| Iron |
Iron of 62 - 72 % |
| Manganese |
Manganese of 0 - 2 % |
| Molybdenum |
Molybdenum of 2 - 3 % |
| Nickel |
Nickel of 10 - 14 % |
| Nitrogen |
Nitrogen of 0 - 0.1 % |
| Phosphorus |
Phosphorus of 0 - 0.05 % |
| Silicon |
Silicon of 0 - 1 % |
| Sulfur |
Sulfur of 0 - 0.03 % |
AISI 316 Cold Finished electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
AISI 316 Cold Finished mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 37 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 520 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 410 MPa |
- |